Microstructure–performance relationships of sPEEK-based catalyst layers

  1. Get@NRC: Microstructure–performance relationships of sPEEK-based catalyst layers (Opens in a new window)
DOIResolve DOI: http://doi.org/10.1149/1.3454735
AuthorSearch for: ; Search for: ; Search for: ; Search for: ; Search for:
Journal titleJournal of The Electrochemical Society
Subjectcatalysts; crystal microstructure; humidity; particle size; porous materials; protein exchange membrane fuel cells; sorption
AbstractPorous catalyst layers containing sulfonated polyetheretherketone (sPEEK, 1.4 meq g− ¹ ) were deposited onto membranes to form catalyst-coated membranes. The catalyst layer properties, as a function of sPEEK content, were studied ex situ and in fuel cells. Particle sizes observed for sPEEK-catalyst inks were smaller than for corresponding Nafion-catalyst inks. Consequently, particle sizes in spray-coated catalyst layers were also smaller. Catalyst layers containing sPEEK were observed to densify with increasing ionomer content in contrast to Nafion-catalyst layers. The catalyst layer thickness decreased from 14 to 4μm when the sPEEK content was increased from 10 to 40 wt %. Pore volumes also decreased and were lower than Nafion-catalyst layers. The optimum sPEEK content of the cathode layer for membrane electrode assemblies was 20 wt %. Lower sPEEK contents compromised proton conductivity, whereas higher sPEEK contents led to excessive flooding of the cathode. Relative humidity of the gases exerted a strong influence on the cathode and fuel cell performance. Too much hydration resulted in excessive flooding; too little led to a significant loss in proton conductivity. Although this paradox is typical of proton exchange membrane fuel cells, it is exacerbated by sPEEK for which water sorption and proton conductivity are highly sensitive to external conditions.
Publication date
AffiliationNRC Institute for Fuel Cell Innovation; National Research Council Canada
Peer reviewedYes
NPARC number23000554
Export citationExport as RIS
Report a correctionReport a correction
Record identifier171c7ad3-8c80-4fd9-95e2-18f2b4fcee69
Record created2016-07-29
Record modified2016-07-29
Bookmark and share
  • Share this page with Facebook (Opens in a new window)
  • Share this page with Twitter (Opens in a new window)
  • Share this page with Google+ (Opens in a new window)
  • Share this page with Delicious (Opens in a new window)