Polymer electrolyte membranes derived from new sulfone monomers with pendent sulfonic acid groups

Download
  1. (PDF, 1 MB)
  2. Get@NRC: Polymer electrolyte membranes derived from new sulfone monomers with pendent sulfonic acid groups (Opens in a new window)
DOIResolve DOI: http://doi.org/10.1021/ma102107a
AuthorSearch for: ; Search for: ; Search for: ; Search for: ; Search for:
TypeArticle
Journal titleMacromolecules
Volume43
Issue23
Pages98109820; # of pages: 11
AbstractNew monomers containing two or four pendent phenyl groups were synthesized by bromination of bis(4-fluorophenyl) sulfone, followed by Suzuki coupling with benzeneboronic acid. The resulting monomers were converted to the corresponding sulfonated monomers having two or four pendent sulfonic acid groups, predominately at the p-phenyl position. Aromatic nucleophilic substitution (SNAr) polycondensation using the di- and tetrasulfonated monomers provided sulfonated poly(arylene ether sulfone) copolymers S2-PAES-xx and S4-PAES-xx, respectively, where xx refers to the molar ratio of the sulfonated to non-sulfonated pendent phenyl monomer. Copoly(arylene ether sulfone)s based on the corresponding nonsulfonated monomers were also synthesized for a parallel study on postpolymerization sulfonation of these copolymers. Postsulfonation occurred predominately at the para-pendent phenyl site, and the reactions were complete within a short time (about 30 min), without evidence of chain degradation. Flexible and tough membranes having high mechanical strength were obtained by solution casting of all four series of copolymers. The copolymers with two or four pendent sulfonic acid groups had high proton conductivities in the range of 44-142 mS/cm for S2-PAES-xx and 51-158 mS/cm for S4-PAES-xx at room temperature, respectively. The methanol permeabilities of these copolymers were in the range of 0.8 x 10-8-15.0 x 10-7 cm2/s, which is lower than Nafion (16.7 x 10-7 cm2/s). The S4-PAES-xx membranes displayed better properties (lower water uptake and higher proton conductivities) than the S2-PAES-xx membranes, which can be attributed to the more blocky architecture of the sulfonic acid groups in the S4 membranes. A combination of high proton conductivities, low water uptake, and low methanol permeabilities for some of the obtained copolymers indicated that they are good candidate materials for proton exchange membrane in fuel cell applications.
Publication date
LanguageEnglish
AffiliationNational Research Council Canada (NRC-CNRC); NRC Institute for Chemical Process and Environmental Technology
Peer reviewedYes
NRC number52238
NPARC number16507157
Export citationExport as RIS
Report a correctionReport a correction
Record identifiere3c4a15b-42ae-4f5f-995b-8c6e5b0221cd
Record created2010-12-21
Record modified2016-05-10
Bookmark and share
  • Share this page with Facebook (Opens in a new window)
  • Share this page with Twitter (Opens in a new window)
  • Share this page with Google+ (Opens in a new window)
  • Share this page with Delicious (Opens in a new window)