Effect of precyclic loading on stress-corrosion-cracking initiation in an X-65 pipeline steel exposed to near-neutral pH soil environment

Download
  1. Get@NRC: Effect of precyclic loading on stress-corrosion-cracking initiation in an X-65 pipeline steel exposed to near-neutral pH soil environment (Opens in a new window)
DOIResolve DOI: http://doi.org/10.1007/s11661-003-0019-y
AuthorSearch for: ; Search for: ; Search for: ; Search for: ; Search for: ; Search for:
TypeArticle
Journal titleMetallurgical and Materials Transactions A
ISSN1073-5623
1543-1940
Volume34
Issue11
Pages26012608
AbstractA study was carried out to understand the effect of precyclic loading on stress-corrosion-crack initiation in an X-65 pipeline steel exposed to a near-neutral-pH soil environment. The test specimens were precyclically loaded before corrosion exposure to represent a service history of up to about 20 years, depending on the severity of pressure fluctuation. Microcracks had initiated on the polished surface of the X-65 pipeline steel after long-time exposure at open-circuit potential (OCP) in a near-neutral-pH synthetic soil solution. These microcracks were mostly initiated from pits at metallurgical discontinuities such as grain boundaries, pearlitic colonies, and banded phases in the steel. Strong preferential dissolution was observed along planes of the banded structures in the steel. The selective corrosion attack at these metallurgical discontinuities is attributed to the galvanic nature of those areas to their neighbors. Cyclic loading prior to corrosion exposure had significant effects on microcrack initiation and propagation during subsequent corrosion exposure. Cyclic loading prior to corrosion exposure either reduced or increased the probability of crack initiation and the rate of crack propagation, depending upon the magnitude of the stress cycles. The largest reduction was seen at a peak cyclic stress of about 0.8 of the yield strength. This cyclic-loading-dependent cracking behavior might be related to the alteration of the substructures and the residual stress in the steel as a result of precyclic loading.
Publication date
PublisherSpringer
LanguageEnglish
AffiliationNational Research Council Canada
Peer reviewedYes
NPARC number23001907
Export citationExport as RIS
Report a correctionReport a correction
Record identifieree39c3bc-2786-4a9e-9c1f-139319b9d7ed
Record created2017-05-23
Record modified2017-05-23
Bookmark and share
  • Share this page with Facebook (Opens in a new window)
  • Share this page with Twitter (Opens in a new window)
  • Share this page with Google+ (Opens in a new window)
  • Share this page with Delicious (Opens in a new window)