Laser cladding of MMC coatings on aluminium substrate : Influence of composition and microstructure on mechanical properties

Télécharger
  1. (PDF, 4 Mo)
  2. Obtenir@CNRC : Laser cladding of MMC coatings on aluminium substrate : Influence of composition and microstructure on mechanical properties (Ouvre dans une nouvelle fenêtre)
DOITrouver le DOI : http://doi.org/10.1016/j.wear.2004.12.010
AuteurRechercher : ; Rechercher : ; Rechercher : ; Rechercher :
TypeArticle
Titre de la revueWear (Amsterdam, Netherlands)
Volume258
Numéro11-12
Pages17451754; nbre. de pages : 10
SujetCrack; Ball on disk testing; Wear test; Hardness test; X ray diffraction; Optical microscopy; Volume fraction; Titanium carbide; Dispersion reinforced material; Bearing(mechanics); Aluminium base alloys; Metal matrix composite; Laser; Aluminium; Composite coating; Content; Wear resistance; Adhesive wear; Hardness; Mechanical properties; Microstructure; Concentration effect; Composition effect; Laser welding; MMC; laser cladding; ball-on-disk wear test; coatings; powders
RésuméThe influence of the composition and the microstructure of laser cladded metal matrix composite (MMC) coatings on their mechanical properties (namely hardness and adhesive wear resistance) was investigated in this study. Laser cladding on pure Al substrate was carried out using a continuous wave (cw) Nd:YAG laser and a coaxial powder injection system. Composite coatings were based on an Al metallic matrix bearing a Si content ranging from 0 to 40 wt.% Si and reinforced with TiC particles with a volume fraction ranging from 0 to 30%. The coating microstructure was characterised by optical microscopy and XRD. Mechanical properties of the samples were determined by hardness and adhesive wear testing. The microstructure of the coatings was homogeneous and free of pores or cracks. Carbides were uniformly distributed throughout the coating cross-section. The addition of Si and TiC reinforcement particles increases the bulk hardness of the coatings and strongly influences the wear mechanism. Indeed, depending on the TiC volume fraction and Si content, the coating wear, characterised by a ball-on-disk device, appeared as mild, severe or surface fatigue wear.
Date de publication
Langueanglais
AffiliationConseil national de recherches Canada
Publications évaluées par des pairsNon
Numéro du CNRC46919
Numéro NPARC12929268
Exporter la noticeExport en format RIS
Signaler une correctionSignaler une correction
Identificateur de l’enregistrementb692ecb2-97a5-4dec-b436-9860fad4ac3e
Enregistrement créé2009-11-16
Enregistrement modifié2016-05-09
Mettre en signet et diffuser
  • Partagez cette page avec Facebook (Ouvre dans une nouvelle fenêtre)
  • Partagez cette page avec Twitter (Ouvre dans une nouvelle fenêtre)
  • Partagez cette page avec Google+ (Ouvre dans une nouvelle fenêtre)
  • Partagez cette page avec Delicious (Ouvre dans une nouvelle fenêtre)