Cyclic Dwell Fatigue Behaviour of Single Crystal Ni-Base Superalloys with/without Rhenium

DOIResolve DOI:
AuthorSearch for: ; Search for: ; Search for: ; Search for:
TypeBook Chapter
Book titleSuperalloys 2012
Pages501508; # of pages: 8
AbstractIn this study, compressive dwell (C-D) and no-dwell (N-D) lowcycle fatigue (LCF) behaviours of several single crystal Ni-base superalloys, including CMSX-4, LSC-11 and LSC-15, were studied under strain-controlled zero-compression (R, = -co) loading at 1100°C. LSC-11 and LSC-15 are new alloys developed by IHI Corporation, Japan with 0.8 wt% Re and without Re addition, respectively, as reduced-cost alternatives to the second generation single crystal Ni-base superalloys. The fatigue experiments were conducted with or without a two-minute dwell (hold) in compression and total strain ranges of 0.7%, 0.6% and 0.5% on uncoated specimens in the [001] orientation. Examination of the cyclic stress-strain behavior revealed that the initially compressive mean stress relaxed to approximately zero stress in N-D tests, while compressive hold resulted in the development of a tensile mean stress during C-D fatigue. Cyclic stress softening was observed under all test conditions. Microstructural analysis of tested specimens showed that N-D fatigue promoted isotropic coarsening of the γ' precipitates, while C-D loading resulted in the formation of discontinuous γ' rafting parallel to the loading direction. Fatigue cracks initiated from the specimen surface from regions of localized oxide attack. All alloys were compressive dwell sensitive. C-D fatigue lives were 4-15x shorter than N-D when the same alloys were considered. CMSX-4 exhibited 1.5-3* N-D fatigue life advantage over alloys LSC-11 and LSC-15. Under C-D fatigue the life advantage of CMSX-4 was 20-50% greater than alloys LSC-11 and LSC-15. The differences in these behaviours could be attributed to Re content and oxidation. © 2012 The Minerals, Metals, & Materials Society. All rights reserved.
Publication date
AffiliationNational Research Council Canada (NRC-CNRC); Aerospace (AERO-AERO)
Peer reviewedYes
NPARC number21269181
Export citationExport as RIS
Report a correctionReport a correction
Record identifier70a5d643-fd75-403b-bc54-626b1dde8af4
Record created2013-12-12
Record modified2016-05-09
Bookmark and share
  • Share this page with Facebook (Opens in a new window)
  • Share this page with Twitter (Opens in a new window)
  • Share this page with Google+ (Opens in a new window)
  • Share this page with Delicious (Opens in a new window)